WW25RR010FTLJ datasheet(6/8 Pages) WALSIN

6 / 8 page

Approval sheet

Page 6 of 7

ASC_WW25R_J_AUTO_V01

JULY -2015

TEST AND REQUIREMENTS

TEST

PROCEDURE

REQUIREMENT

High temperature exposure

MIL-STD-202-108

Ambient temperature 155

±2°C, no load, 1000 hrs

no visible damage

∆R/R max. ±3%

Temperature cycling

JESD22 JA-104

30 minutes at -55

°C±3°C,

2~3 minutes at room temperature,

30 minutes at +125

°±3°C,

2~3 minutes at room temperature,

Total 1000 continuous cycles

no visible damage

∆R/R max. ±1%

Bias Humidity

MIL-STD-202-103

Condition

: 85°C ＆ 85% R.H.

Test power

: 10% of rated power shall be applied

continuously. Duration 1000hrs

no visible damage

∆R/R max. ±3%

Operational Life

MIL-STD-202-108

Ambient temperature: 125±2ºC

The applied voltage shall be the voltage to be

calculated at 35% of rated dissipation or the

limiting

element

voltage

whichever

the

smaller.

Condition: The voltage shall be applied continuously.

Duration: 1000 hrs

no visible damage

∆R/R max. ±3%

Dimension

JESD22 Method JB-100

Meet dimension spec as

defined in p.3

Resistance to Solvents

MIL-STD-202-215

Solvent: 2−propanol at 25℃

Immersion time: 3 min

Brush: 10 times brushing

Immersion and brush cycle: 3cycle

∆R/R: max ±1%

No visible damage

Mechanical Shock

MIL-STD-202-213

Waveform:

half sine,

Peak value

100G,

Normal duration

6ms

Condition: XX'YY'ZZ', 10times each

∆R/R: max. ±1%

No visible damage

Vibration

MIL-STD-202-204

Peak acceleration and Sweep time:

5 g's for 20

min , Frequency 10Hz to 2000Hz,

Condition: 12 cycles each of 3 orientations

∆R/R: max ±1%

No visible damage

Resistance to soldering heat

MIL-STD-202-210

Un-mounted chips 10±0.5 seconds, 260±5ºC

∆R/R: max ±1%

No visible damage

ESD test

AEC Q200-002

Human body model, 2 Kohm, 150 pF,

Test voltage: 8KV

∆R/R: max ±1%

No visible damage

Solderability

J-STD-002

a)4hrs / 155℃*dry then solder dipping 235℃/5sec

b)Steam 8 hrs then 215℃ / 5sec solder dipping

c)Steam 8 hrs then 260℃ / 7sec solder dipping

good tinning (>95%

covered)

no visible damage

Bending strength

AEC Q200-005

Bending 2mm for 60 seconds.

∆R/R: max ±1%

No visible damage

Adhesion

AEC Q200-006

Pressurizing force: 17.7N, Test time: 60±1s.

∆R/R: max ±1%

No visible damage

WW25RR010FTLJ Datasheet(PDF) 6 Page - WALSIN TECHNOLOGY CORPORATION